The objective of this work was to evaluate biaxial-flexural-strength (σf), Vickers hardness (HV), fracture toughness (K Ic), Young's modulus (E), Poisson's ratio (ν) and porosity (P) of two commercial glass-ceramics, Empress (E1) and Empress 2 (E2), as a function of the hot-pressing temperature. Ten disks were hot-pressed at 1065, 1070, 1075 and 1080 °C for E1; and at 910, 915, 920 and 925 °C for E2. The porosity was measured by an image analyzer software and s f was determined using the piston-on-three-balls method. K Ic and HV were determined by an indentation method. Elastic constants were determined by the pulse-echo method. For E1 samples treated at different temperatures, there were no statistical differences among the values of all evaluated properties. For E2 samples treated at different temperatures, there were no statistical differences among the values of σf, E, and ν, however HV and K Ic were significantly higher for 910 and 915 °C, respectively. Regarding P, the mean value obtained for E2 for 925 °C was significantly higher compared to other temperatures.

The ferroelectric compound LiNbO3 was prepared by the polymeric precursors method in the polycrystalline form containing different concentrations of Eu3+. The compounds were characterized by X-ray diffraction, vibrational and electronic spectroscopy. Electronic spectroscopy was shown to be sensitive to small concentrations of contaminating phases allowing a good control of the compound purity. The presence of Eu3+ ions leads to the formation of the LiNb3O8 phase in the range of 500 to 800 °C. Above this temperature range LiNbO3 and tetragonal (T') EuNbO4 were obtained.